Chemical Composition
Chemical Composition
|
CHEMICAL COMPOSITION ( IN PERCENTAGE ) |
||||||||||
|
Grade |
C (Max) |
Mn (Max) |
P (Max) |
S (Max) |
Si (Max) |
Cr |
Ni |
Mo |
Nitrogen (Max) |
Cu/ Others |
|
301 |
0.15 |
2.00 |
0.045 |
0.030 |
1.00 |
16.00 - 18.00 |
6.00 - 8.00 |
- |
0.10 |
- |
|
304 |
0.08 |
2.00 |
0.045 |
0.030 |
0.75 |
18.00 - 20.00 |
8.00- 10.50 |
- |
0.10 |
- |
|
304L |
0.030 |
2.00 |
0.045 |
0.030 |
0.75 |
18.00 - 20.00 |
8.00- 12.00 |
- |
0.10 |
- |
|
310S |
0.08 |
2.00 |
0.045 |
0.030 |
1.50 |
24.00- 26.00 |
19.00 - 22.00 |
- |
- |
- |
|
316 |
0.08 |
2.00 |
0.045 |
0.030 |
0.75 |
16.00 - 18.00 |
10.00 - 14.00 |
2.00 - 3.00 |
0.10 |
- |
|
316L |
0.030 |
2.00 |
0.045 |
0.030 |
0.75 |
16.00 - 18.00 |
10.00 - 14.00 |
2.00 - 3.00 |
0.10 |
- |
|
317 |
0.08 |
2.00 |
0.045 |
0.030 |
0.75 |
18.00 - 20.00 |
11.00 - 14.00 |
3.00 - 4.00 |
0.10 |
- |
|
317L |
0.030 |
2.00 |
0.045 |
0.030 |
0.75 |
18.00 - 20.00 |
11.00 - 15.00 |
3.00 - 4.00 |
0.10 |
- |
|
321 |
0.08 |
2.00 |
0.045 |
0.030 |
0.75 |
17.00 - 19.00 |
9.00 - 12.00 |
- |
0.10 |
Ti5 ( C + N ) Min or 0.70 max |
|
347 |
0.08 |
2.00 |
0.045 |
0.030 |
0.75 |
17.00 - 19.00 |
9.00 - 13.00 |
- |
- |
Cb= 10x ( C Min ) or 1.00 Max |
|
409 |
0.08 |
1.00 |
0.040 |
0.010 |
1.00 |
10.50 - 11.75 |
0.50 |
- |
- |
Ti= 6x (C+ N ) Min or 0.70 Max |
|
409M |
0.03 |
0.81.2 |
0.030 |
0.030 |
0.40.75 |
11.00- 12.00 |
1.5 max. |
- |
- |
Ti= 6x (C) Min or 0.70 Max |
|
410S |
0.08 |
1.00 |
0.040 |
0.030 |
1.00 |
11.50- 13.50 |
0.60 |
- |
- |
- |
|
410 |
0.15 |
1.00 |
0.040 |
0.030 |
1.00 |
11.50- 13.50 |
0.75 |
- |
- |
- |
|
420 |
0.35 |
0.50 |
0.035 |
0.015 |
0.50 |
12.00 - 13.00 |
0.20.3 |
- |
- |
- |
|
430 |
0.12 |
1.00 |
0.040 |
0.030 |
1.00 |
16.00 - 18.00 |
0.75 |
- |
- |
- |
|
JSL AUS |
0.08 |
7.08.0 |
0.070 |
0.030 |
0.75 |
15.50 - 16.50 |
4.25 - 4.75 |
- |
- |
0.9 - 1.10 |
|
JS- 203 |
0.08 |
9.2510.25 |
0.070 |
0.030 |
0.75 |
14.25 - 15.25 |
2.25 - 2.75 |
- |
- |
1.60- 2.0 |
|
301M |
0.10 |
4.55.5 |
0.060 |
0.030 |
0.75 |
14.50 - 15.50 |
6.0 - 7.0 |
- |
- |
1.70- 1.90 |
|
* Thickness of 1.27mm & below will have elongation of 20% min. |
||||||||||
Duplex
| S31803 / S32205 | C | N | P | Si | Mn | Mo | Fe | Cr | S | Ni |
| 1.0 | 0.03 | 0.02 | 2.0 | 3.0 - 3.5 | 22.0 - 23.0 | 0.03 | 4.5 - 6.5 | 0.14 - 0.2 | Bal |
Super Duplex
| S32750 / S32760 | C | N | P | Si | Mn | Mo | Ni | Cr | S | Other |
| 0.030 | 0.24/0.32 | 0.035 | 0.80 | 1.20 | 3.0/5.0 | 6.00/8.00 | 24.0/26.0 | 0.020 | Cu:0.50 |
Hastelloy
| Hastelloy C276 | Ni | C | Mo | Mn | Si | Fe | P | S | Co | Cr |
| Balance | 0.01 max | 15 - 17 | 1.0 max | 0.08 max | 4 - 7 | 0.04 max | 0.03 max | 2.5 max | 14.5 - 16.5 |
Nickel
| Grade | C | Mn | Si | Fe | S | Cr2 | Al-Ti | Ni | |
| 625 | min. | – | – | – | – | – | 20.0 | – | 58.0 |
| max. | 0.10 | 0.50 | 0.50 | 5.0 | 0.015 | 23.0 | 0.40 | – | |
904L
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 904L | 490 | 220 | 35 | 70-90 typical | – |